Product Description
STWD6006 elastic waterproof coating material takes one-component environmental-friendly water-borne polymer resin as main raw material, and refined through scientific production process. The coating is compact, has strong adhesion with various kinds of substrates. It has excellent sealing and impermeability, good hiding power, excellent anti-aging performance, it will not peel off or powder after long-term outdoor use. It has excellent waterproof protection on building surfaces, which has been widely used in Europe and the United States.
Product features:
- The film is compact and has good adhesion force, integral forming waterproof system
- Excellent anti-aging performance, long-term outdoor use will not fall off, or powder or color-changing, it will extend the service life.
- Excellent flexibility in low temperature, -40 Centigrade
- Anticorrosion and chemical resistance
- Excellent waterproof, anti-mildew performance
- Water based coating, environmentally friendly, toxic free, safe material.
- Easy to apply, it is a replacement product to tar-based polyurethane waterproof coating
Product application scope
Concrete roof, steel roof, kitchen bathroom floor, bathroom, reservoir, basement, waterproof membrane and old roof SBS waterproof and renovation works (such as asphalt, PVC, SBS, polyurethane and other base)
Product information
| Item |
Results |
|
| Appearance |
White or gray |
|
| Glossy |
Matte |
|
| specific gravity (g/cm3) |
1.12 |
|
| Viscosity (cps )@20ºC |
420 |
|
| Solid content (%) |
71%±2% |
|
| surface dry time (h) |
Summer: 1-2h, winter: 2-4h |
|
| theoretical coverage |
0.17kg/m2(thickness 100um) |
Physical property
| Item |
Test standard |
Results |
| Hiding power (white or light color)/(g/m²) |
JG/T235-2008 |
≤150 |
| Dry time/h |
JG/T172-2005 |
Surface dry time≤2; solid dry time≤24 |
| Adhesion (cross cut method) / grade |
JG/T172-2005 |
≤1 |
| Impermeability |
JG/T172-2005 |
0.3MPa/30min, Impermeable |
| Impact resistance /cm |
JG/T172-2005 |
≥30 |
| Tensile strength |
JG/T172-2005 |
≥1.7Mpa |
| Elongation rate |
JG/T172-2005 |
≥200% |
| Tear resistance,≥kN/m |
JG/T172-2005 |
35 |
| Temperature resistance of coating (5 cycles) |
JG/T172-2005 |
Normal |
Corrosion resistance property
| Acid resistance c(5%H2SO4) |
JG/T172-2005 |
168 h, normal |
| Salt spray resistance |
JG/T172-2005 |
1000 h , no peel off, no peel off |
| Artificial accelerated anti-aging (1000h) |
Tensile strength retention, % |
85 |
| Elongation rate, % |
≥150 |
Application environment
Environment temperature: 5-35ºC
Humidity: ≤85%
Application instructions
Recommended dft (1layer) 200-300um
Recoating time (25ºC) Min:4h, Max: 28h
Recommended application method Roller, brush
Application tips
The surface should be clean, without any oil, rust or dusts.
The remaining material is not allowed to pour back to the original drums.
It is water-based coating, don't add other organic solvents or other coatings in it.
Product curing time
Substrate temperature surface dry time foot traffic solid dry
25ºC 40 min 12h 7d
Product storage and shelf life
Storage temperature:+5-35°C
Shelf life: 12 months (unsealed)
Keep the products seal well, store in cool and ventilated place, avoid direct sunshine exposure.
Package: 20kg/drum
Product health and safety information
For information and advice on the safe handling, storage and disposal of chemical products, users shall refer to the latest Material Safety Data Sheet containing physical, ecological, toxicological and other safety related data.
Integrity declaration
STWD guarantee all technical data stated in this sheet are based on laboratory tests. Actual testing methods may vary due to different circumstances. Therefore please test and verify its applicability. STWD does not take any other responsibilities except the product quality and reserve the right of any modifications on the listed data without prior notice.