STWD9013 floor special polyurea is 100% solid content aromatic polyurea elastomer. It has excellent flexibility and abrasion resistance, compared with traditional epoxy and carborundum floor coating be too hard and fragile, this coating is impact resistance and wearable. It also has been used on the food processing and pharmaceutical flooring field because it is 100% solid content, without solvent.
Product features and advantages
*Solvent free, 100% solid content, safe, environmentally friendly and odor free.
*Rapid cure, can be sprayed forming on any bent, slope and vertical surfaces, no sagging.
*Dense coating, seamless, with good flexibility, good adhesive strength
*Excellent impact resistance, abrasion resistance
*Excellent corrosion resistance and chemical resistance to acids, alkali, salts etc.
*Excellent waterproof performance
*Good shock absorbing performance
*Excellent resistance to temperature variation
*Fast cure, application site back to service quickly
*Excellent durability to reduce maintenance cost of service life
*Extend the service life of sprayed structure
Application scope
Petrochemical, metallurgical machinery, food processing, pharmaceutical, electronics, textile, garment and other industries engineering workshop floor. Stadiums, parking lots, supermarkets, department stores, municipal Footbridge flooring project.
Products information
| Item | Part A | Part B |
| Appearance | Pale yellow liquid |
Adjustable |
| Specific gravity (g/m³) | 1.12 | 1.05 |
| Viscosity(cps)@25ºC | 800 | 650 |
| Solid content (%) | 100 | 100 |
| Mix ratio(volume ratio) | 1 | 1 |
| Gel time(second)@25ºC | 4-6 | |
| Surface dry time(second) | 15-40 | |
| theoretical coverage (dft) | 1.02kg/m2 film thickness:1mm | |
| Item | ASTM D-2240 | 90 |
| Hardness (Shore A) | ASTM D-412 | 470 |
| Elongation rate(%) | ASTM D-412 | 19 |
| Tensile strength(Mpa) | ASTM D-624 | 65 |
| Tear strength (kN/m) | HG/T 3831-2006 | impermeable |
| Impermeability(0.3Mpa/30min) | HG/T 3831-2006 | 4.2 |
| Wear resistance(750g/500r)/mg | HG/T 3831-2006 | 3.4 |
| Adhesive strength(Mpa)concrete base | HG/T 3831-2006 | 11.1 |
| Adhesive strength(Mpa) steel base | GB/T 6750-2007 | 1.02 |
| Density(g/cm³) | HG/T 3831-2006 | ≤15mm |
| Cathodic disbondment [1.5v,(65±5)ºC,48h] | ASTM D-2240 | 90 |
| Acid resistance 10%H2SO4 or 10%HCI,30d | No rust, no bubbles, no peel off |
| Alkali resistance 10% NaOH, 30d | No rust, no bubbles, no peel off |
| Salt resistance 30g/L,30d | No rust, no bubbles, no peel off |
| Salt spray resistance, 2000h | No rust, no bubbles, no peel off |
| Oil resistance 0# d iesel, crude,30d | No rust, no bubbles, no peel off |
| (For reference: the above data is acquired based on GB / T9274-1988 test standard. Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data) | |