STWD9003 sewage water treatment pool special polyurea is a 100% solid content aromatic polyurea elastomer. It it stable in anticorrosion property, suitable for corrosion environment, with superior anticorrosion effect than traditional anticorrosion material which can greatly improve the surface life of sewage pools. It has been widely used in the sewage treatment pool project in home and abroad.
Product features and advantages
*Solvent free, 100% solid content, safe, environmentally friendly and odor free.
*Rapid cure, can be sprayed forming on any bent, slope and vertical surfaces, no sagging.
*Dense coating, seamless, with good flexibility.
*High adhesive strength, can fast bond well on many substrate like steel, concrete, wood, fiber glass etc.
*Excellent impact resistance and abrasion resistance
*Excellent anticorrosion, chemical resistance to acid, alkali and salt.
*excellent impervious and waterproof performance
*Good shock absorbing performance
*Excellent resistance to temperature variation
*Fast cure, application site back to service quickly
*Excellent durability to reduce maintenance cost of service life
*Extend the service life of sprayed structure
Product Applications
Anticorrosion waterproof protection on various industrial and urban sewage water treatment pools
Products information
| Item |
A |
B |
| Appearance |
Pale yellow liquid |
Adjustable color |
| Specific gravity (g/m³) |
1.13 |
1.05 |
| Viscosity(cps)@25ºC |
810 |
660 |
| Solid content (%) |
100 |
100 |
| Mix ratio(by volume) |
1 |
1 |
| Gel time(second)@25ºC |
4-6 |
| Surface dry time(second) |
15-40 |
| Theoretical Coverage(dft) |
1.06kg/m2 film thickness:1mm |
Physical properties of products
| Item |
Test standard |
Result |
| Hardness (Shore A) |
ASTM D-2240 |
92 |
| Elongation rate(%) |
ASTM D-412 |
460 |
| Tensile strength(Mpa) |
ASTM D-412 |
17 |
| Tear strength (kN/m) |
ASTM D-624 |
68 |
| Impermeability(0.3Mpa/30min) |
HG/T 3831-2006 |
impermeable |
| Wearable(750g/500r)/mg |
HG/T 3831-2006 |
4.5 |
| Adhesive strength(Mpa)concrete base |
HG/T 3831-2006 |
3.1 |
| Adhesive strength(Mpa) steel base |
HG/T 3831-2006 |
11 |
| Density(g/cm³) |
GB/T 6750-2007 |
1.02 |
| Cathodic disbondment [1.5v,(65±5)ºC,48h] |
HG/T 3831-2006 |
≤15mm |
| Item |
A |
B |
| Appearance |
Pale yellow liquid |
Adjustable color |
| Specific gravity (g/m³) |
1.12 |
1.05 |
| Viscosity(cps)@25ºC |
790 |
640 |
| Solid content (%) |
100 |
100 |
| Mix ratio(by volume) |
1 |
1 |
| Gel time(second)@25ºC |
4-6 |
| Surface dry time(second) |
15-40 |
| Theoretical Coverage(dft) |
1.08kg/m2Film thickness 1mm |
| Item |
Test standard |
Result |
| Hardness (Shore A) |
ASTM D-2240 |
90 |
| Elongation rate(%) |
ASTM D-412 |
460 |
| Tensile strength(Mpa) |
ASTM D-412 |
17 |
| Tear strength (kN/m) |
ASTM D-624 |
63 |
| Impermeability(0.3Mpa/30min) |
HG/T 3831-2006 |
Impermeable |
| Wearable(750g/500r)/mg |
HG/T 3831-2006 |
4.4 |
| Adhesive strength(Mpa)concrete base |
HG/T 3831-2006 |
3.1 |
| Adhesive strength(Mpa) steel base |
HG/T 3831-2006 |
11 |
| Density(g/cm³) |
GB/T 6750-2007 |
1.02 |
| Cathodic disbondment [1.5v,(65±5)ºC,48h] |
HG/T 3831-2006 |
≤15mm |
Product features and advantages
*Solvent free, 100% solid content, safe, environmentally friendly and odor free.
*Rapid cure, can be sprayed forming on any bent, slope and vertical surfaces, no sagging.
*Dense coating, seamless, with good flexibility.
*
*High adhesive strength, can fast bond well on many substrate like steel, concrete, wood, fiber glass etc.
*
*Excellent impact resistance and abrasion resistance
*Excellent anticorrosion, chemical resistance to acid, alkali and salt.
*excellent impervious and waterproof performance
*Good shock absorbing performance
*
*Excellent resistance to temperature variation
*Fast cure, application site back to service quickly
*Excellent durability to reduce maintenance cost of service life
*Extend the service life of sprayed structure