Flame Retardant Polyurea Anti-Corrosion Protective Coating for Traffic Tunnels

• CAS No.: 9007
• Color: All Color Can Offer
• Appearance: Liquid
• Main Raw Material: Polyurethane
• Method: Spray
• Level: Finish Coat
• Model NO.: 9007
• Drying Method: Chemical Mechanical Curing
• Certification: ISO14001, ISO9001
• Substrate: Steel
• Components: Film Forming Matter
• Formation Mechanism: Conversion Type
• Transport Package: Barrel/Pallet
• Specification: 210L
• Trademark: STWD
• Origin: China
• Production Capacity: 80000pieces/Year

Product Description

Product descriptions    STWD9007 traffic tunnel special fire retardant polyurea is a 100% solid content aromatic polyurea elastomer. It not only has excellent physical properties of polyurea, but also can extinguish right after being deviated from fire, now it has been widely applied in Chinese tunnel projects.
 

 

Product features and advantages
*Solvent free, 100% solid content, safe, environmentally friendly and odor free.
*Rapid cure, can be sprayed forming on any bent, slope and vertical surfaces, no sagging.
*Dense coating, seamless, with good flexibility

 

 

 

*High adhesive strength, can fast bond well on many substrate like steel, concrete, wood, fiber glass etc.
*Excellent impact resistance, abrasion resistance

 

*Excellent corrosion resistance and chemical resistance to acids, alkali, salts etc.
*Excellent waterproof performance

 

*Good shock absorbing performance

 

*Excellent resistance to temperature variation
*Fast cure, application site back to service quickly
*Excellent durability to reduce maintenance cost of service life
*Extend the service life of sprayed structure

 

 

 

,.

 

Chnpn yìngyòng fànwéi
jiànzhú, huàgōng, jiāotōng, yějīn, diànlì, hángtiān, hiyáng, chuánbó děng zhòngduō lngyù de fángf fángshu fánghù.
: ,,,,
: ,,,,
Product Applications
Fire retardant anticorrosion waterproof protection of railways, road, urban subway and other transportation facilities.
 

 

Products information

Item	A	B
Appearance	Pale yellow liquid	Adjustable color
Specific gravity (g/m³)	1.15	1.2
Viscosity (cps) @25ºC	700	680
Solid content (%)	100	100
Mix ratio (by volume)	1	1
Gel time (second) @25ºC	4-6
Surface dry time (second)	15-40
Theoretical Coverage (dft)	1.08kg/ Film thickness 1mm

Physical properties 

Item	Test standard	Result
Hardness (Shore A)	ASTM D-2240	92
Elongation rate(%)	ASTM D-412	450
Tensile strength(Mpa)	ASTM D-412	16
Tear strength (N/km)	ASTM D-624	62
Impermeability(0.3Mpa/30min)	HG/T 3831-2006	impermeable
Wearable(750g/500r)/mg	HG/T 3831-2006	4.6
Adhesive strength(Mpa)concrete base	HG/T 3831-2006	3
Adhesive strength(Mpa) steel base	HG/T 3831-2006	11
Density(g/cm³)	GB/T 6750-2007	1.1
Cathodic disbondment [1.5v,(65±5)ºC,48h]	HG/T 3831-2006	≤15mm

Chemical resistance

Acid resistance 10%H2SO4 or 10%HCI,30d	No rust, no bubbles, no peel off
Alkali resistance 10% NaOH, 30d	No rust, no bubbles, no peel off
Salt resistance 30g/L,30d	No rust, no bubbles, no peel off
Salt spray resistance, 2000h	No rust, no bubbles, no peel off
Oil resistance 0# diesel, crude,30d	No rust, no bubbles, no peel off
(For reference: the above data is acquired based on GB / T9274-1988 test standard. Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data)

Product application environment

Environment temperature	0ºC-45ºC
Product spray heating temperature	65ºC-70ºC
hose heating temperature	55ºC-65ºC
Relative humidity	≤90%
Dew point	≥3ºC

Product application guide

Recommend spray machine	H-XP3 Polyurea spray equipment
Spray gun	Fusion-air purge or mechanical purge
Static pressure	2300-2500psi
Dynamic pressure	2000-2200psi
Recommend film thickness	1000-3000μm
Recoating interval	≤6h

Application note

1. Agitate part B uniform prior to application, thoroughly mix the deposited pigments, or the product quality will be affected.

1. spray polyurea within the proper time if the substrate surface is primed. For the application method and interval time of STWD polyurea special primer please refer to STWD companies' other brochure.
2. Always apply STWD spray polyurea on a small area before large application to check the mix ratio, color and spray effect are correct. For detailed information of application please refer to the latest instruction sheet of the application instructions of STWD spray polyurea series.

Product curing time

Substrate temperature	Dry	Walking intensity	complete solidify
+10ºC	30s	45min	7d
+20ºC	23s	15min	6d
+30ºC	17s	5min	5d

Note: the curing time varies with the environment condition especially the temperature and relative humidity.

Shelf Life
* From the manufacturer date and on the original package sealed condition:
Part A: 10 months
Part B: 10 months
*storage temperature:+5-35°C
Packing: Part A 220kg/drum, part B 200kg/drum
Make sure the product package sealed well
* store in cool and ventilated place, avoid direct sunshine exposure.

Product health and safety information  
For information and advice on the safe handling, storage and disposal of chemical products, users shall refer to the most recent Material Safety Data Sheet containing physical, ecological, toxicological and other safety related data.

Integrity declaration    
STWD guarantee all technical data stated in this sheet are based on laboratory tests. Actual testing methods may vary due to different circumstances. Therefore please test and verify its applicability. STWD does not take any other responsibilities except the product quality and reserve the right of any modifications on the listed data without prior notice.