STWD8027 is a two-component material with aliphatic polyaspartic polyurea resin as the main film-forming material, with excellent corrosion resistance, color-change resistance and weather resistance. The product has high solid and low viscosity, good leveling, and meets the requirements of environmental protection; it has excellent workability, can be applied by any application method, and can be cured at low temperature 0 ° C in winter. The coating has excellent flexibility, wear resistance, impact resistance and chemical resistance. It is an ideal weather resistant and environment-friendly floor coating material.
Features and benefits
* high solids low density, with good leveling, the coating film is tough, dense, full light and bright colors
* high adhesive strength, good compatible with polyurethane, epoxy and other coating film.
* high hardness, good scratch resistance and stain resistance
* excellent abrasion resistance, impact resistance
* excellent anticorrosion property, resist to acid, alkali, salt and others.
* no discoloration, UV resistance, no yellowing, no powdering, aging resistance, with excellent weather resistance and gloss and color retention property
* can be applied directly to the surface of metal surface (DTM)
* this product is environmentally friendly and contains no benzene solvents and lead compounds
Product application scope
Flooring of city Park Plaza, electronic plant, mechanical factory, chemical plant, pharmaceutical, food and other industrial floors, as well as various outdoor yellowing resistant and wear-resistant floors.
Product information
| Item | A component | B component |
| Appearance | light yellow liquid | Color adjustable |
| Specific gravity(g/m³) | 1.04 | 1.50 |
| Viscosity (cps)@25ºC | 40-60 | 100-200 |
| Solid content (%) | 65 | 88 |
| Mix ratio (by weight) | 1 | 1 |
| Surface dry time (h) | 1 | |
| Pot life (h)@25ºC | 40min | |
| Theoretical coverage (DFT) | 0.15kg/m2 film thickness 100μm | |
| Item | Test standard | Results |
| Adhesion force (concrete base) | 3Mpa | |
| Pencil hardness | 2H | |
| Bending resistance (cylindrical) | ≤1mm | |
| Abrasion resistance (750g/500r) mg | HG/T 3831-2006 | 5 |
| Impact resistance kg·cm | GB/T 1732 | 50 |
| Anti-aging, artificial accelerated aging | GB/T14522-1993 | Light loss < 1, pulverization < 1 |
| Acid resistance 30%H2SO4 or 10%HCI, 240h | no rust, no bubbles, no peel off |
| Alkali resistance 30%NaOH, 240h | no rust, no bubbles, no peel off |
| Salt resistance 30g/L, 240h | no rust, no bubbles, no peel off |
| Salt spray resistance 1500h | no rust, no bubbles, no peel off |
| Oil resistance, 0# d iesel, oil | no rust, no bubbles, no peel off |
| Waterproof, 48h | No bubbles, no wrinkled, no color-changing, no peel off |
| Note: the above chemical medium resistance performance is obtained according to the test method of GB / T9274-1988 and is only for reference. Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data | |
| environment temperature | -5~+35ºC |
| humidity | ≤85% |
| dew point | ≥3ºC |
Application instructions
Hand brush, roller
Air spray, with air pressure 0.3-0.5Mpa
Airless spray, with spray pressure 15-20Mpa
Recommend dft: 100-200μm (topcoat)
Recoating interval: min 2h, max 24h.