STWD9007 traffic tunnel special fire retardant polyurea is a 100% solid content aromatic polyurea elastomer. It not only has excellent physical properties of polyurea, but also can extinguish right after being deviated from fire, now it has been widely applied in Chinese tunnel projects.
Product features and advantages
*Solvent free, 100% solid content, safe, environmentally friendly and odor free.
*Rapid cure, can be sprayed forming on any bent, slope and vertical surfaces, no sagging.
*Dense coating, seamless, with good flexibility
*High adhesive strength, can fast bond well on many substrate like steel, concrete, wood, fiber glass etc.
*Excellent impact resistance, abrasion resistance
*Excellent corrosion resistance and chemical resistance to acids, alkali, salts etc.
*Excellent waterproof performance
*Good shock absorbing performance
*Excellent resistance to temperature variation
*Fast cure, application site back to service quickly
*Excellent durability to reduce maintenance cost of service life
*Extend the service life of sprayed structure
Product Applications
Fire retardant anticorrosion waterproof protection of railways, road, urban subway and other transportation facilities.
Products information
| Item | A | B |
| Appearance | Pale yellow liquid | Adjustable color |
| Specific gravity (g/m³) | 1.15 | 1.2 |
| Viscosity (cps) @25ºC | 700 | 680 |
| Solid content (%) | 100 | 100 |
| Mix ratio (by volume) | 1 | 1 |
| Gel time (second) @25ºC | 4-6 | |
| Surface dry time (second) | 15-40 | |
| Theoretical Coverage (dft) | 1.08kg/m2 Film thickness 1mm | |
| Item | Test standard | Result |
| Hardness (Shore A) | ASTM D-2240 | 92 |
| Elongation rate(%) | ASTM D-412 | 450 |
| Tensile strength(Mpa) | ASTM D-412 | 16 |
| Tear strength (N/km) | ASTM D-624 | 62 |
| Impermeability(0.3Mpa/30min) | HG/T 3831-2006 | impermeable |
| Wearable(750g/500r)/mg | HG/T 3831-2006 | 4.6 |
| Adhesive strength(Mpa)concrete base | HG/T 3831-2006 | 3 |
| Adhesive strength(Mpa) steel base | HG/T 3831-2006 | 11 |
| Density(g/cm³) | GB/T 6750-2007 | 1.1 |
| Cathodic disbondment [1.5v,(65±5)ºC,48h] | HG/T 3831-2006 | ≤15mm |
| Acid resistance 10%H2SO4 or 10%HCI,30d | No rust, no bubbles, no peel off |
| Alkali resistance 10% NaOH, 30d | No rust, no bubbles, no peel off |
| Salt resistance 30g/L,30d | No rust, no bubbles, no peel off |
| Salt spray resistance, 2000h | No rust, no bubbles, no peel off |
| Oil resistance 0# d iesel, crude,30d | No rust, no bubbles, no peel off |
| (For reference: the above data is acquired based on GB / T9274-1988 test standard. Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data) | |