One Component Waterproof UV Resistance Paint Coating for Building Roof and Walls Protection

• Color: White
• Appearance: Liquid
• Main Raw Material: Acrylic
• Method: Brush
• Level: Finish Coat
• Drying Method: Drying
• Model NO.: 6006
• Certification: ISO14001, ISO9001
• Substrate: Concrete
• Components: Film Forming Matter
• Formation Mechanism: Conversion Type
• Transport Package: Barrel
• Specification: 25L
• Trademark: STWD
• Origin: China
• HS Code: 3208201090
• Production Capacity: 80, 000kg/Week

Product Description

STWD6006 elastic waterproof coating material takes one-component environmental-friendly water-borne polymer resin as main raw material, and refined through scientific production process. The coating is compact, has strong adhesion with various kinds of substrates. It has excellent sealing and impermeability, good hiding power, excellent anti-aging performance, it will not peel off or powder after long-term outdoor use. It has excellent waterproof protection on building surfaces, which has been widely used in Europe and the United States.

Product features:

• The paint coating is compact and has good adhesion force, integral forming waterproof system
• Excellent anti-aging performance, long-term outdoor use will not fall off, or powder or color-changing, it will extend the service life.
• Excellent flexibility in low temperature, -40 Centigrade
• Anticorrosion and chemical resistance
• Excellent waterproof, anti-mildew performance
• Water based coating, environmentally friendly, toxic free, safe material.
• Easy to apply, it is a replacement product to tar-based polyurethane waterproof coating

Product application scope
Concrete roof, steel roof, kitchen bathroom floor, bathroom, reservoir, basement, waterproof membrane and old roof SBS waterproof and renovation works (such as asphalt, PVC, SBS, polyurethane and other base)

Product information

Item	Results
Appearance	White or gray
Glossy	Matte
specific gravity (g/cm^3)	1.12
Viscosity (cps )@20ºC	420
Solid content (%)	71%±2%
surface dry time (h)	Summer: 1-2h, winter: 2-4h
theoretical coverage	0.17kg/m^2(thickness 100um)

                    
Physical property

Item	Test standard	Results
Hiding power (white or light color)/(g/m²)	JG/T235-2008	≤150
Dry time/h	JG/T172-2005	Surface dry time≤2; solid dry time≤24
Adhesion (cross cut method) / grade	JG/T172-2005	≤1
Impermeability	JG/T172-2005	0.3MPa/30min, Impermeable
Impact resistance /cm	JG/T172-2005	≥30
Tensile strength	JG/T172-2005	≥1.7Mpa
Elongation rate	JG/T172-2005	≥200%
Tear resistance,≥kN/m	JG/T172-2005	35
Temperature resistance of coating (5 cycles)	JG/T172-2005	Normal

Corrosion resistance property

Acid resistance ^c(5%H2SO4)	JG/T172-2005	168 h, normal
Salt spray resistance	JG/T172-2005	1000 h , no peel off, no peel off
Artificial accelerated anti-aging  (1000h)	Tensile strength retention, %	85
	Elongation rate, %	≥150

Application environment
Environment temperature: 5-35ºC
Humidity: ≤85%