Product Description
STWD6006 elastic waterproof coating material takes one-component environmental-friendly water-borne polymer resin as main raw material, and refined through scientific production process. The coating is compact, has strong adhesion with various kinds of substrates. It has excellent sealing and impermeability, good hiding power, excellent anti-aging performance, it will not peel off or powder after long-term outdoor use. It has excellent waterproof protection on building surfaces, which has been widely used in Europe and the United States.
Product features:
- The film is compact and has good adhesion force, integral forming waterproof system
- Excellent anti-aging performance, long-term outdoor use will not fall off, or powder or color-changing, it will extend the service life.
- Excellent flexibility in low temperature, -40 Centigrade
- Anticorrosion and chemical resistance
- Excellent waterproof, anti-mildew performance
- Water based coating, environmentally friendly, toxic free, safe material.
- Easy to apply, it is a replacement product to tar-based polyurethane waterproof coating
Product application scope
Concrete roof, steel roof, kitchen bathroom floor, bathroom, reservoir, basement, waterproof membrane and old roof SBS waterproof and renovation works (such as asphalt, PVC, SBS, polyurethane and other base)
Product information
| Item |
Results |
|
| Appearance |
White or gray |
|
| Glossy |
Matte |
|
| specific gravity (g/cm3) |
1.12 |
|
| Viscosity (cps )@20ºC |
420 |
|
| Solid content (%) |
71%±2% |
|
| surface dry time (h) |
Summer: 1-2h, winter: 2-4h |
|
| theoretical coverage |
0.17kg/m2(thickness 100um) |
Physical property
| Item |
Test standard |
Results |
| Hiding power (white or light color)/(g/m²) |
JG/T235-2008 |
≤150 |
| Dry time/h |
JG/T172-2005 |
Surface dry time≤2; solid dry time≤24 |
| Adhesion (cross cut method) / grade |
JG/T172-2005 |
≤1 |
| Impermeability |
JG/T172-2005 |
0.3MPa/30min, Impermeable |
| Impact resistance /cm |
JG/T172-2005 |
≥30 |
| Tensile strength |
JG/T172-2005 |
≥1.7Mpa |
| Elongation rate |
JG/T172-2005 |
≥200% |
| Tear resistance,≥kN/m |
JG/T172-2005 |
35 |
| Temperature resistance of coating (5 cycles) |
JG/T172-2005 |
Normal |
Corrosion resistance property
| Acid resistance c(5%H2SO4) |
JG/T172-2005 |
168 h, normal |
| Salt spray resistance |
JG/T172-2005 |
1000 h , no peel off, no peel off |
| Artificial accelerated anti-aging (1000h) |
Tensile strength retention, % |
85 |
| Elongation rate, % |
≥150 |
Application environment
Environment temperature: 5-35ºC
Humidity: ≤85%