Product Description
STWD9002 Power plant water tank special polyurea is a 100% solid content aromatic polyurea elastomer material. The product has excellent adhesive strength, dense and seamless, also have good anticorrosion, waterproof, moisture-proof and impermeability. It has been widely used in the demineralized water tank projects in home and abroad.
Product features and advantages
*Solvent free, 100% solids, safe, environmentally friendly and odor free.
*Rapid cure, can be sprayed forming on any bent, slope and vertical surfaces, no sagging.
*Dense coating, seamless, with good flexibility.
*Excellent impact resistance, abrasion resistance
*Excellent anticorrosion and chemical resistance to acids, alkali, salts etc.
*Excellent waterproof performance
*Good shock absorbing performance
*Excellent resistance to temperature variation
*Fast cure, application site back to service quickly
*Excellent durability to reduce lifelong maintenance cost
*Extend the service life of sprayed structure
Application scopes
Anticorrosion waterproof protection of demineralized water tanks, storage tanks, towers and other facilities in power plant industry.
Product information
| Item |
A |
B |
| Appearance |
Pale yellow liquid |
Adjustable color |
| Specific gravity (g/m³) |
1.12 |
1.05 |
| Viscosity(cps)@25ºC |
790 |
640 |
| Solid content (%) |
100 |
100 |
| Mix ratio(by volume) |
1 |
1 |
| Gel time(second)@25ºC |
4-6 |
| Surface dry time(second) |
15-40 |
| Theoretical Coverage(dft) |
1.08kg/m2Film thickness 1mm |
Physical properties
| Item |
Test standard |
Result |
| Hardness (Shore A) |
ASTM D-2240 |
90 |
| Elongation rate(%) |
ASTM D-412 |
460 |
| Tensile strength(Mpa) |
ASTM D-412 |
17 |
| Tear strength (kN/m) |
ASTM D-624 |
63 |
| Impermeability(0.3Mpa/30min) |
HG/T 3831-2006 |
Impermeable |
| Wearable(750g/500r)/mg |
HG/T 3831-2006 |
4.4 |
| Adhesive strength(Mpa)concrete base |
HG/T 3831-2006 |
3.1 |
| Adhesive strength(Mpa) steel base |
HG/T 3831-2006 |
11 |
| Density(g/cm³) |
GB/T 6750-2007 |
1.02 |
| Cathodic disbondment [1.5v,(65±5)ºC,48h] |
HG/T 3831-2006 |
≤15mm |
Chemical resistance
| Acid resistance 10%H2SO4 or 10%HCI,30d |
No rust, no bubbles, no peel off |
| Alkali resistance 10% NaOH, 30d |
No rust, no bubbles, no peel off |
| Salt resistance 30g/L,30d |
No rust, no bubbles, no peel off |
| Salt spray resistance, 2000h |
No rust, no bubbles, no peel off |
| Oil resistance 0# d iesel, crude, 30d |
No rust, no bubbles, no peel off |
| (For reference: the above data is acquired based on GB / T9274-1988 test standard. Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data) |
Product application environment
| Environment temperature |
0ºC-45ºC |
| Product spray heating temperature |
65ºC-70°C |
| hose heating temperature |
55ºC-65ºC |
| Relative humidity |
≤90% |
| Dew point |
≥3ºC |
Product application guide
| Recommend spray machine |
GRA CO H-XP3 Polyurea spray equipment |
| Spray gun |
Fusion-air purge or mechanical purge |
| Static pressure |
2300-2500psi |
| Dynamic pressure |
2000-2200psi |
| Recommend film thickness |
1000-3000μm |
| Recoating interval |
≤6h |
Application note
- Agitate part B uniform prior to application, thoroughly mix the deposited pigments, or the product quality will be affected.
- spray polyurea within the proper time if the substrate surface is primed. For the application method and interval time of STWD polyurea special primer please refer to STWD company's other brochure.
- Always apply STWD polyurea on a small area before large application to check the mix ratio, color and spray effect are correct. For detailed information of application please refer to the latest instruction sheet of the application instructions of STWD spray polyurea series.
Product curing time
| Substrate temperature |
Dry |
Walking intensity |
complete solidify |
| +10ºC |
30s |
45min |
7d |
| +20ºC |
21s |
15min |
6d |
| +30ºC |
19s |
5min |
5d |
Note: the curing time varies with the environment condition especially the temperature and relative humidity.
Shelf Life
* From the manufacturer date and on the original package sealed condition:
Part A: 10 months
Part B: 10 months
*storage temperature:+5-35°C
Packing: Part A 220kg/drum, part B 200kg/drum
Make sure the product package sealed well
* store in cool and ventilated place, avoid direct sunshine exposure.