STWD8003 takes fluo rine copolymer resin or fluorinated olefins and other monomer copolymer as main film material, produced from scientific process. The two component anticorrosion decoration topcoat has large amount of C-F bond which is known to be the strongest molecular bond, therefore it has incomparable properties of durability, weather resistance, chemical resistance, non-stick, self-lubricating and anti-radiation.
Product features and advantages
* coating film is compact tough, full shine and colorful
* no yellowing, no powdery, no crack and anti-aging, with excellent weather resistance and color-keep property
* excellent adhesive strength, with good compatible with polyurethane, epoxy, chlorinated rubber, alkyd, phenolic and other coatings
* excellent abrasion resistance, bending and impact resistance
* excellent heat resistance and cold tolerance
* excellent chemical resistance such as acid, alkali and salt
* excellent anticorrosion property
* excellent waterproof property
* excellent durability to reduce the maintenance cost for lifelong
* extend the service life of sprayed structure
Typical use
Anti-corrosion protection, decoration works of construction, road and bridge, municipal engineering, stadiums, petrochemical, electrical and electronic industry, machinery industry, aviation and other fields.
Product information
| Item | Part A | Part B |
| Appearance | Light yellow liquid | Color adjustable |
| Specific gravity (g/cm3 ) | 1.32 | 1.04 |
| Viscosity (cps) at 25ºC | 720 | 570 |
| Solid content (%) | 58 | 58 |
| Mix ratio (by weight) | 1 | 1 |
| Gel time (second) @25ºC | ||
| surface dry tme (h) | 3-12h | |
| Re-coat time (h) | Min 3h, Max unlimited (20ºC) | |
| theoretical coverage (dft) | 0.11kg/m2 (thickness 50um) | |
| Item | Test standard | Results |
| Pencil hardness | GB/T 6739-2006 | 2H |
| Adhesive strength (grid method) | GB/T 1720-1989 | 1 grade |
| Flexibility | GB/T 1731-1993 | 1 grade |
| Impact resistance kg·cm | GB/T 1731-1993 | 50kg·cm |
| Weather resistance, artificial accelerated aging 1000h | GB/T14522-1993 | Loss of light <1, powdery <1 |
| Acid resistance 10%H2SO4 or 6%HCl,60d | no rust, no bubbles, no peel off |
| Alkali resistance 10%NaOH, 60d | no rust, no bubbles, no peel off |
| Salt resistance 50g/L,60d | no rust, no bubbles, no peel off |
| Salt spray resistance, 2000h | no rust, no bubbles, no peel off |
| Organic solvent resistance, 60d | no rust, no bubbles, no peel off |
| Cold and heat resistance (10 times) | no bubbles, no wrinkle, no discoloration, no peel off |
| (For reference: Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data) | |
Application environment
Environment temperature: 0 ~ 35ºC
Relative humidity: ≤80%
Dew point: ≥3ºC
Application tips
Hand brush, roller
Air spray, air pressure 0.3-0.5Mpa
Airless spray, spray pressure 15-20Mpa
Recommended dft: 30-60 um
Re-coating interval: ≥3h